钕铁硼牌号
牌号 | 剩磁感应强度(Br) | 内禀矫顽力Hcj | 磁感 | 最大磁能积 | 最高工作温度 |
| mT(KGS)) | kA/m (kOe) | kA/m(kOe) | kJ/m3(MGOe)) | ℃ |
N38 | 1220-1250 | ≥955 | ≥899 | 287-310 | 80 |
| 12.2-12.5 | ≥12 | ≥11.3 | 36-39 |
|
N42 | 1280-1320 | ≥955 | ≥915 | 318-342 | 80 |
| 12.8-13.2 | ≥12 | ≥11.5 | 40-43 |
|
N45 | 1320-1380 | ≥955 | ≥923 | 342-366 | 80 |
| 13.2-13.8 | ≥12 | ≥11.6 | 43-46 |
|
N50 | 1400-1450 | ≥876 | ≥796 | 382-406 | 80 |
| 14-14.5 | ≥11 | ≥10 | 48-51 |
|
38M | 1220-1250 | ≥1114 | ≥899 | 287-310 | 100 |
| 12.2-12.5 | ≥14 | ≥11.3 | 36-39 |
|
42M | 1280-1320 | ≥1114 | ≥955 | 318-342 | 100 |
| 12.8-13.2 | ≥14 | ≥12 | 40-43 |
|
45M | 1320-1380 | ≥1114 | ≥995 | 342-366 | 100 |
| 13.2-13.8 | ≥14 | ≥12.5 | 43-46 |
|
48M | 1360-1430 | ≥1114 | ≥1027 | 366-390 | 100 |
| 13.6-14.3 | ≥14 | ≥12.9 | 46-49 |
|
35H | 1170-1220 | ≥1353 | ≥868 | 263-287 | 120 |
| 11.7-12.2 | ≥17 | ≥10.9 | 33-36 |
|
38H | 1220-1250 | ≥1353 | ≥899 | 287-310 | 120 |
| 12.2-12.5 | ≥17 | ≥11.3 | 36-39 |
|
40H | 1250-1280 | ≥1353 | ≥923 | 302-326 | 120 |
| 12.5-12.8 | ≥17 | ≥11.6 | 38-41 |
|
42H | 1280-1320 | ≥1353 | ≥995 | 318-342 | 120 |
| 12.8-13.2 | ≥17 | ≥12 | 40-43 |
|
45H | 1300-1360 | ≥1353 | ≥963 | 326-3658 | 120 |
| 13-13.6 | ≥17 | ≥12.1 | 43-46 |
|
35SH | 1170-1220 | ≥1592 | ≥876 | 263-287 | 150 |
| 11.7-12.2 | ≥20 | ≥11 | 33-36 |
|
38SH | 1220-1250 | ≥1592 | ≥907 | 287-310 | 150 |
| 12.2-12.5 | ≥20 | ≥11.4 | 36-39 |
|
40SH | 1240-1280 | ≥1592 | ≥939 | 302-326 | 150 |
| 12.4-12.8 | ≥20 | ≥11.8 | 38-41 |
|
42SH | 1280-1320 | ≥1592 | ≥987 | 318-342 | 150 |
| 12.8-13.2 | ≥20 | ≥12.4 | 40-43 |
|
35UH | 1180-1220 | ≥1990 | ≥860 | 263-287 | 180 |
| 11.8-12.2 | ≥12.5 | ≥10.8 | 33-36 |
|
38UH | 1220-1250 | ≥1990 | ≥876 | 287-310 | 180 |
| 12.2-12.5 | ≥12.5 | ≥11 | 36-39 |
|
33EH | 1130-1170 | ≥2388 | ≥836 | 243-271 | 200 |
| 11.3-11.7 | ≥30 | ≥10.5 | 31-34 |
|
35EH | 1170-1220 | ≥2388 | ≥876 | 263-287 | 200 |
| 11.7-12.2 | ≥30 | ≥11 | 33-36 |
|
铝镍钴牌号
特性 | 最大磁能积(BH) | 顽磁 | 矫顽力 | 内禀矫顽力Hcj | 密度d | 温度系数(Br) | 居里温度Tc |
牌号 | kJ/m3(MGOe)) | mT(kG) | kA/m(kOe) | kA/m(kOe) | g/cm3 | %/K | ℃ |
SAlNiCo14/5 | 13-15 | 730-800 | 47-50 | 50-53 | 7.1 | -0.02 | 790 |
SAlNiCo14/6 | 14-15 | 620-810 | 56-64 | 58-66 | 7.1 | -0.02 | 790 |
SAlNiCo14/8 | 14-16 | 550-610 | 75-88 | 80-92 | 7.1 | -0.01 | 850 |